Elettrodi tal-forn tal-ark elettriku elettrodi rp hp uhp grad
| Oġġett | Unità | Rp | Hp | UHP | ||||
| 250-400 | 450-800 | 300-400 | 450-700 | 300-400 | 450-700 | |||
| Reżistività elettrika | Elettrodu | μΩ.m | 7.5-8.6 | 7.5-8.8 | 5.5-6.8 | 5.5-7.0 | 4.6-6.0 | 4.8-6.2 |
| Bżieżel | 4.5-5.5 | 4.0-5.0 | 3.5-4.5 | |||||
| Qawwa tal-liwi | Elettrodu | MPA | Akbar minn jew daqs 8.0 | Akbar minn jew daqs 11.0 | Akbar minn jew daqs 11.0 | |||
| Bżieżel | Akbar minn jew daqs 15.0 | Akbar minn jew daqs 16.0 | Akbar minn jew daqs 18.0 | |||||
| Modulu elastiku | Elettrodu | GPA | Inqas minn jew daqs 9.0 | Inqas minn jew daqs 11.0 | Inqas minn jew daqs 13.0 | |||
| Bżieżel | Inqas minn jew daqs 13.0 | Inqas minn jew daqs 14.0 | Inqas minn jew daqs 15.0 | |||||
| Densità tal-massa | Elettrodu | g / cm3 | 1.55-1.65 | 1.63-1.73 | 1.65-1.75 | |||
| Bżieżel | 1.70-1.75 | 1.73-1.80 | 1.75-1.82 | |||||
| Irmied | Elettrodu | % | Inqas minn jew daqs 0.3 | |||||
| Bżieżel | ||||||||
| CTE (100-600) ºC | Elettrodu | 10-6/ºC | 2.00-2.50 | 1.80-2.00 | 1.30-1.50 | |||
| Bżieżel | 1.50-1.80 | 1.50-1.80 | 1.20-1.40 | |||||
Merħba biex tikkuntattjana għall-kwotazzjoni.
X'inhuma l-elettrodi tal-grafita tal-forn tal-ark elettriku (EAF), u x'inhuma l-gradi RP, HP, u UHP?
L-elettrodi tal-grafita tal-forn tal-ark elettriku huma komponenti konduttivi kritiċi fl-EAFs, użati biex jiġġeneraw temperaturi għoljin (sa 3,000 grad) għall-azzar tal-fdal tat-tidwib u metalli oħra. Huma magħmula minn grafita ta 'purità għolja -, magħżula għall-konduttività termali u elettrika eċċellenti tagħha, reżistenza għal xokk termali, u saħħa mekkanika.
It-tikkettiRP (qawwa regolari), HP (Qawwa Għolja), UUHP (qawwa ultra għolja)Jindikaw gradi ta 'prestazzjoni distinti, definiti minn parametri tekniċi ewlenin bħal reżistività, densità tal-massa, u saħħa tal-flexural. Dawn il-gradi jirriflettu direttament il-kapaċità tal-elettrodi li jimmaniġġjaw il-kurrent, l-effiċjenza fl-enerġija, u d-durabilità fl-operazzjonijiet tal-EAF:
Grad RP:Iddisinjat għal ext jew inqas - POWER EAFS (tipikament<50 MW), RP electrodes have higher resistivity (~65–75 μΩ·m), lower bulk density (~1.68–1.70 g/cm³), and moderate flexural strength (~7 MPa). They are cost-effective but less efficient, suitable for smaller-scale or legacy steelmaking setups where energy savings are secondary to upfront cost.
Grad HP:Inġinerija għal nofs - firxa EAFs (50–80 MW), l-elettrodi HP għandhom reżistività mnaqqsa (~ 55-65 μω · m), densità ogħla (~ 1.70–1.72 g / cm³), u saħħa mtejba (~ 8 MPA). Huma jtejbu l-effiċjenza fl-enerġija b'10-15% meta mqabbla ma 'RP, u jnaqqsu l-vit - għal - TIPT TIMES u jestendu l-ħajja tal-elettrodi b'20-30%, u jagħmilhom ideali għall-immodernizzar ta' faċilitajiet anzjani.
Grad UHP: Reserved for large, high-power EAFs (>80 MW), l-elettrodi UHP għandhom ultra - reżistività baxxa (<55 μΩ·m), superior density (>1.72 g/cm³), and exceptional strength (>10 MPa). Huma jippermettu tħaddim stabbli f'densitajiet ta 'kurrent għoli (sa 100 ka), qtugħ tap - sa -} Tekt tal-ħinijiet b'25-30% u l-konsum ta' elettrodi bi 30-40%. Dan jagħmilhom indispensabbli għall-iskala kbira -, għolja - Produttività tal-Pjanti tal-Azzar li jipprijoritizzaw l-effiċjenza u s-sostenibbiltà.
It-tags Popolari: Elettrodi tal-Furnaħ tal-Arka Elettrika RP HP UHP Grad, China Electric Arc Furnace Elettrodi tal-Grafita RP HP UHP Grad Manifatturi, Fornituri, Fabbrika